AWS BVAg-32 vs. Z41121 Zinc

AWS BVAg-32 belongs to the otherwise unclassified metals classification, while Z41121 zinc belongs to the zinc alloys. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-32 and the bottom bar is Z41121 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
87
Poisson's Ratio 0.37
0.25
Shear Modulus, GPa 34
35
Tensile Strength: Ultimate (UTS), MPa 180
140

Thermal Properties

Latent Heat of Fusion, J/g 140
110
Melting Completion (Liquidus), °C 950
410
Melting Onset (Solidus), °C 900
400
Specific Heat Capacity, J/kg-K 270
390
Thermal Expansion, µm/m-K 17
26

Otherwise Unclassified Properties

Density, g/cm3 11
6.6

Common Calculations

Stiffness to Weight: Axial, points 4.9
7.4
Stiffness to Weight: Bending, points 14
23
Strength to Weight: Axial, points 4.7
6.1
Strength to Weight: Bending, points 6.7
9.3
Thermal Shock Resistance, points 8.0
4.6

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Cadmium (Cd), % 0 to 0.0010
0 to 0.0050
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 20 to 22
0.080 to 0.49
Iron (Fe), % 0
0 to 0.010
Lead (Pb), % 0 to 0.0020
0 to 0.010
Palladium (Pd), % 23 to 27
0
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 53 to 55
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0
0.050 to 0.18
Zinc (Zn), % 0 to 0.0010
99.292 to 99.87