AWS BVAg-6b vs. CR022A Copper

AWS BVAg-6b belongs to the otherwise unclassified metals classification, while CR022A copper belongs to the copper alloys. They have 50% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-6b and the bottom bar is CR022A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
120
Poisson's Ratio 0.35
0.34
Shear Modulus, GPa 35
43
Tensile Strength: Ultimate (UTS), MPa 180
230

Thermal Properties

Latent Heat of Fusion, J/g 160
210
Melting Completion (Liquidus), °C 870
1090
Melting Onset (Solidus), °C 780
1040
Specific Heat Capacity, J/kg-K 310
390
Thermal Expansion, µm/m-K 19
17

Otherwise Unclassified Properties

Density, g/cm3 9.7
9.0
Embodied Carbon, kg CO2/kg material 49
2.6
Embodied Energy, MJ/kg 770
41

Common Calculations

Stiffness to Weight: Axial, points 5.3
7.2
Stiffness to Weight: Bending, points 16
18
Strength to Weight: Axial, points 5.1
7.1
Strength to Weight: Bending, points 7.3
9.3
Thermal Shock Resistance, points 7.4
8.1

Alloy Composition

Antimony (Sb), % 0
0 to 0.00040
Arsenic (As), % 0
0 to 0.00050
Bismuth (Bi), % 0
0 to 0.00020
Cadmium (Cd), % 0 to 0.0010
0 to 0.00010
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 49 to 51
99.99 to 99.999
Iron (Fe), % 0
0 to 0.0010
Lead (Pb), % 0 to 0.0020
0 to 0.00050
Manganese (Mn), % 0
0 to 0.00050
Nickel (Ni), % 0
0 to 0.0010
Phosphorus (P), % 0 to 0.0020
0.0010 to 0.0060
Selenium (Se), % 0
0 to 0.00020
Silver (Ag), % 49 to 51
0 to 0.0025
Sulfur (S), % 0
0 to 0.0015
Tellurium (Te), % 0
0 to 0.00020
Tin (Sn), % 0
0 to 0.00020
Zinc (Zn), % 0 to 0.0010
0 to 0.00010