AWS BVAg-6b vs. Solder Alloy 121

Both AWS BVAg-6b and solder alloy 121 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-6b and the bottom bar is solder alloy 121.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
21
Poisson's Ratio 0.35
0.43
Shear Modulus, GPa 35
7.5
Tensile Strength: Ultimate (UTS), MPa 180
32

Thermal Properties

Latent Heat of Fusion, J/g 160
29
Melting Completion (Liquidus), °C 870
290
Melting Onset (Solidus), °C 780
230
Specific Heat Capacity, J/kg-K 310
140
Thermal Expansion, µm/m-K 19
28

Otherwise Unclassified Properties

Density, g/cm3 9.7
11
Embodied Carbon, kg CO2/kg material 49
5.6
Embodied Energy, MJ/kg 770
93

Common Calculations

Stiffness to Weight: Axial, points 5.3
1.1
Stiffness to Weight: Bending, points 16
8.6
Strength to Weight: Axial, points 5.1
0.84
Strength to Weight: Bending, points 7.3
2.1
Thermal Shock Resistance, points 7.4
3.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0 to 0.0010
0 to 0.0050
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 49 to 51
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0 to 0.0020
83.4 to 85.5
Nickel (Ni), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 49 to 51
0 to 0.1
Tin (Sn), % 0
14.5 to 15.5
Zinc (Zn), % 0 to 0.0010
0 to 0.0010