AWS BVAg-6b vs. Solder Alloy 141

Both AWS BVAg-6b and solder alloy 141 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-6b and the bottom bar is solder alloy 141.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
37
Poisson's Ratio 0.35
0.39
Shear Modulus, GPa 35
13
Tensile Strength: Ultimate (UTS), MPa 180
54

Thermal Properties

Latent Heat of Fusion, J/g 160
46
Melting Completion (Liquidus), °C 870
190
Melting Onset (Solidus), °C 780
180
Specific Heat Capacity, J/kg-K 310
180
Thermal Expansion, µm/m-K 19
24

Otherwise Unclassified Properties

Density, g/cm3 9.7
8.9
Embodied Carbon, kg CO2/kg material 49
11
Embodied Energy, MJ/kg 770
180

Common Calculations

Stiffness to Weight: Axial, points 5.3
2.3
Stiffness to Weight: Bending, points 16
13
Strength to Weight: Axial, points 5.1
1.7
Strength to Weight: Bending, points 7.3
3.6
Thermal Shock Resistance, points 7.4
4.3

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
2.0 to 3.0
Cadmium (Cd), % 0 to 0.0010
0 to 0.0020
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 49 to 51
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0 to 0.0020
35.9 to 38.5
Nickel (Ni), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 49 to 51
0 to 0.1
Tin (Sn), % 0
59.5 to 60.5
Zinc (Zn), % 0 to 0.0010
0 to 0.0010