AWS BVAg-6b vs. Solder Alloy 703

Both AWS BVAg-6b and solder alloy 703 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-6b and the bottom bar is solder alloy 703.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
51
Poisson's Ratio 0.35
0.36
Shear Modulus, GPa 35
19
Tensile Strength: Ultimate (UTS), MPa 180
57

Thermal Properties

Latent Heat of Fusion, J/g 160
61
Melting Completion (Liquidus), °C 870
220
Melting Onset (Solidus), °C 780
220
Specific Heat Capacity, J/kg-K 310
220
Thermal Expansion, µm/m-K 19
22

Otherwise Unclassified Properties

Density, g/cm3 9.7
7.4
Embodied Carbon, kg CO2/kg material 49
18
Embodied Energy, MJ/kg 770
300

Common Calculations

Stiffness to Weight: Axial, points 5.3
3.8
Stiffness to Weight: Bending, points 16
17
Strength to Weight: Axial, points 5.1
2.1
Strength to Weight: Bending, points 7.3
4.4
Thermal Shock Resistance, points 7.4
3.7

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0 to 0.0010
0 to 0.0020
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 49 to 51
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0 to 0.0020
0 to 0.070
Nickel (Ni), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 49 to 51
3.3 to 3.7
Tin (Sn), % 0
95.8 to 96.7
Zinc (Zn), % 0 to 0.0010
0 to 0.0010