AWS BVAg-8b vs. AWS BAg-9

Both AWS BVAg-8b and AWS BAg-9 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 85% of their average alloy composition in common. There are 16 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-8b and the bottom bar is AWS BAg-9.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 84
82
Poisson's Ratio 0.36
0.35
Shear Modulus, GPa 31
31
Tensile Strength: Ultimate (UTS), MPa 170
140

Thermal Properties

Brazing Temperature, °C 800 to 900
720 to 840
Latent Heat of Fusion, J/g 140
130
Melting Completion (Liquidus), °C 800
720
Melting Onset (Solidus), °C 780
670
Specific Heat Capacity, J/kg-K 280
290
Thermal Expansion, µm/m-K 19
20

Otherwise Unclassified Properties

Density, g/cm3 10
9.6

Common Calculations

Stiffness to Weight: Axial, points 4.7
4.8
Stiffness to Weight: Bending, points 15
15
Strength to Weight: Axial, points 4.7
4.1
Strength to Weight: Bending, points 6.8
6.3
Thermal Shock Resistance, points 7.6
6.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 26.8 to 29.2
19 to 21
Lead (Pb), % 0 to 0.0020
0
Nickel (Ni), % 0.3 to 0.7
0
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 70.5 to 72.5
64 to 66
Zinc (Zn), % 0 to 0.0010
13 to 17
Residuals, % 0
0 to 0.15