AWS BVAg-8b vs. Reactor Grade Zirconium

Both AWS BVAg-8b and reactor grade zirconium are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-8b and the bottom bar is reactor grade zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 84
98
Poisson's Ratio 0.36
0.34
Shear Modulus, GPa 31
37
Tensile Strength: Ultimate (UTS), MPa 170
330

Thermal Properties

Latent Heat of Fusion, J/g 140
250
Specific Heat Capacity, J/kg-K 280
270
Thermal Expansion, µm/m-K 19
5.9

Otherwise Unclassified Properties

Density, g/cm3 10
6.5

Common Calculations

Stiffness to Weight: Axial, points 4.7
8.4
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 4.7
14
Strength to Weight: Bending, points 6.8
16
Thermal Shock Resistance, points 7.6
41

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 26.8 to 29.2
0
Lead (Pb), % 0 to 0.0020
0
Nickel (Ni), % 0.3 to 0.7
0
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 70.5 to 72.5
0
Zinc (Zn), % 0 to 0.0010
0
Zirconium (Zr), % 0
99.7 to 100
Residuals, % 0
0 to 0.27