AWS BVAu-2 vs. AWS BAg-23
Both AWS BVAu-2 and AWS BAg-23 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition.
For each property being compared, the top bar is AWS BVAu-2 and the bottom bar is AWS BAg-23.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 90 |
| Poisson's Ratio | 0.4 | |
| 0.36 |
| Shear Modulus, GPa | 36 | |
| 33 |
| Tensile Strength: Ultimate (UTS), MPa | 150 | |
| 170 |
Thermal Properties
| Brazing Temperature, °C | 890 to 1010 | |
| 750 to 1040 |
| Latent Heat of Fusion, J/g | 92 | |
| 130 |
| Melting Completion (Liquidus), °C | 890 | |
| 970 |
| Melting Onset (Solidus), °C | 890 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 180 | |
| 270 |
| Thermal Expansion, µm/m-K | 15 | |
| 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.3 | |
| 5.0 |
| Stiffness to Weight: Bending, points | 9.1 | |
| 15 |
| Strength to Weight: Axial, points | 2.4 | |
| 4.7 |
| Strength to Weight: Bending, points | 3.6 | |
| 6.8 |
| Thermal Shock Resistance, points | 7.1 | |
| 6.8 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 19.5 to 20.5 | |
| 0 |
| Gold (Au), % | 79.5 to 80.5 | |
| 0 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 13.9 to 16 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 |
| Silver (Ag), % | 0 | |
| 84 to 86 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |