AWS BVAu-2 vs. Solder Alloy 162

Both AWS BVAu-2 and solder alloy 162 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BVAu-2 and the bottom bar is solder alloy 162.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
35
Poisson's Ratio 0.4
0.4
Shear Modulus, GPa 36
12
Tensile Strength: Ultimate (UTS), MPa 150
41

Thermal Properties

Latent Heat of Fusion, J/g 92
44
Melting Completion (Liquidus), °C 890
220
Melting Onset (Solidus), °C 890
180
Specific Heat Capacity, J/kg-K 180
180
Thermal Expansion, µm/m-K 15
25

Otherwise Unclassified Properties

Density, g/cm3 17
9.3

Common Calculations

Stiffness to Weight: Axial, points 3.3
2.1
Stiffness to Weight: Bending, points 9.1
12
Strength to Weight: Axial, points 2.4
1.2
Strength to Weight: Bending, points 3.6
2.8
Thermal Shock Resistance, points 7.1
3.3

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0 to 0.0010
0 to 0.0020
Carbon (C), % 0 to 0.0050
0
Copper (Cu), % 19.5 to 20.5
1.2 to 1.6
Gold (Au), % 79.5 to 80.5
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0 to 0.0020
47.3 to 49.3
Nickel (Ni), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.0020
0
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
49.5 to 50.5
Zinc (Zn), % 0 to 0.0010
0 to 0.0010