AWS BVAu-4 vs. ASTM B522 Class II

Both AWS BVAu-4 and ASTM B522 class II are otherwise unclassified metals. They have 69% of their average alloy composition in common. There are 15 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BVAu-4 and the bottom bar is ASTM B522 class II.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
96
Poisson's Ratio 0.4
0.41
Shear Modulus, GPa 41
34
Tensile Strength: Ultimate (UTS), MPa 190
280 to 490

Thermal Properties

Latent Heat of Fusion, J/g 100
77
Melting Completion (Liquidus), °C 950
1030
Melting Onset (Solidus), °C 950
1030
Specific Heat Capacity, J/kg-K 190
160
Thermal Expansion, µm/m-K 14
15

Otherwise Unclassified Properties

Density, g/cm3 17
17

Common Calculations

Stiffness to Weight: Axial, points 3.6
3.1
Stiffness to Weight: Bending, points 9.3
8.9
Strength to Weight: Axial, points 3.0
4.4 to 7.8
Strength to Weight: Bending, points 4.2
5.5 to 8.0
Thermal Shock Resistance, points 8.7
13 to 24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0
Gold (Au), % 81.5 to 82.5
68.5 to 69.5
Lead (Pb), % 0 to 0.0020
0
Nickel (Ni), % 17.5 to 18.5
0
Phosphorus (P), % 0 to 0.0020
0
Platinum (Pt), % 0
5.5 to 6.5
Silver (Ag), % 0
24.5 to 25.5
Sulfur (S), % 0
0 to 0.010
Zinc (Zn), % 0 to 0.0010
0
Residuals, % 0
0 to 0.26