AWS BVPd-1 vs. CC753S Brass
AWS BVPd-1 belongs to the otherwise unclassified metals classification, while CC753S brass belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is AWS BVPd-1 and the bottom bar is CC753S brass.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 150 | |
100 |
Poisson's Ratio | 0.37 | |
0.31 |
Shear Modulus, GPa | 56 | |
40 |
Tensile Strength: Ultimate (UTS), MPa | 240 | |
340 |
Thermal Properties
Latent Heat of Fusion, J/g | 200 | |
170 |
Melting Completion (Liquidus), °C | 1240 | |
820 |
Melting Onset (Solidus), °C | 1230 | |
780 |
Specific Heat Capacity, J/kg-K | 310 | |
390 |
Thermal Expansion, µm/m-K | 12 | |
21 |
Otherwise Unclassified Properties
Density, g/cm3 | 11 | |
8.1 |
Common Calculations
Stiffness to Weight: Axial, points | 7.7 | |
7.1 |
Stiffness to Weight: Bending, points | 16 | |
19 |
Strength to Weight: Axial, points | 6.1 | |
12 |
Strength to Weight: Bending, points | 7.9 | |
13 |
Thermal Shock Resistance, points | 9.8 | |
11 |
Alloy Composition
Aluminum (Al), % | 0 | |
0.4 to 0.8 |
Antimony (Sb), % | 0 | |
0 to 0.050 |
Cadmium (Cd), % | 0 to 0.0010 | |
0 |
Carbon (C), % | 0 to 0.0050 | |
0 |
Cobalt (Co), % | 33.9 to 36 | |
0 |
Copper (Cu), % | 0 | |
56.8 to 60.5 |
Iron (Fe), % | 0 | |
0.5 to 0.8 |
Lead (Pb), % | 0 to 0.0020 | |
1.8 to 2.5 |
Manganese (Mn), % | 0 | |
0 to 0.2 |
Nickel (Ni), % | 0 to 0.060 | |
0.5 to 1.2 |
Palladium (Pd), % | 64 to 66 | |
0 |
Phosphorus (P), % | 0 to 0.0020 | |
0 to 0.020 |
Silicon (Si), % | 0 | |
0 to 0.050 |
Tin (Sn), % | 0 | |
0 to 0.8 |
Zinc (Zn), % | 0 to 0.0010 | |
33.1 to 40 |