AWS BVPd-1 vs. Grade 250 Maraging Steel
AWS BVPd-1 belongs to the otherwise unclassified metals classification, while grade 250 maraging steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is AWS BVPd-1 and the bottom bar is grade 250 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 150 | |
| 190 |
| Poisson's Ratio | 0.37 | |
| 0.3 |
| Shear Modulus, GPa | 56 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 240 | |
| 970 to 1800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 270 |
| Melting Completion (Liquidus), °C | 1240 | |
| 1480 |
| Melting Onset (Solidus), °C | 1230 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 310 | |
| 450 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 16 | |
| 23 |
| Strength to Weight: Axial, points | 6.1 | |
| 33 to 61 |
| Strength to Weight: Bending, points | 7.9 | |
| 26 to 40 |
| Thermal Shock Resistance, points | 9.8 | |
| 29 to 54 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.050 to 0.15 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Cadmium (Cd), % | 0 to 0.0010 | |
| 0 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 to 0.030 |
| Cobalt (Co), % | 33.9 to 36 | |
| 7.0 to 8.5 |
| Iron (Fe), % | 0 | |
| 66.3 to 71.1 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 | |
| 4.6 to 5.2 |
| Nickel (Ni), % | 0 to 0.060 | |
| 17 to 19 |
| Palladium (Pd), % | 64 to 66 | |
| 0 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0.3 to 0.5 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |