AWS BVPd-1 vs. N06110 Nickel

AWS BVPd-1 belongs to the otherwise unclassified metals classification, while N06110 nickel belongs to the nickel alloys. There are 15 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BVPd-1 and the bottom bar is N06110 nickel.

AWS BVPd-1 (P03657) Vacuum Service Filler Metal UNS N06110 Nickel Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		150
Elastic (Young's, Tensile) Modulus, GPa		210

Poisson's Ratio		0.37
Poisson's Ratio		0.28

Shear Modulus, GPa		56
Shear Modulus, GPa		84

Tensile Strength: Ultimate (UTS), MPa		240
Tensile Strength: Ultimate (UTS), MPa		730

Thermal Properties

Latent Heat of Fusion, J/g		200
Latent Heat of Fusion, J/g		340

Melting Completion (Liquidus), °C		1240
Melting Completion (Liquidus), °C		1490

Melting Onset (Solidus), °C		1230
Melting Onset (Solidus), °C		1440

Specific Heat Capacity, J/kg-K		310
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Density, g/cm³		11
Density, g/cm³		8.6

Common Calculations

Stiffness to Weight: Axial, points		7.7
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		16
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		6.1
Strength to Weight: Axial, points		23

Strength to Weight: Bending, points		7.9
Strength to Weight: Bending, points		21

Thermal Shock Resistance, points		9.8
Thermal Shock Resistance, points		20

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 1.0

Cadmium (Cd), %		0 to 0.0010
Cadmium (Cd), %		0

Carbon (C), %		0 to 0.0050
Carbon (C), %		0 to 0.15

Chromium (Cr), %		0
Chromium (Cr), %		28 to 33

Cobalt (Co), %		33.9 to 36
Cobalt (Co), %		0

Copper (Cu), %		0
Copper (Cu), %		0 to 0.5

Iron (Fe), %		0
Iron (Fe), %		0 to 1.0

Lead (Pb), %		0 to 0.0020
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		9.0 to 12

Nickel (Ni), %		0 to 0.060
Nickel (Ni), %		51 to 62

Niobium (Nb), %		0
Niobium (Nb), %		0 to 1.0

Palladium (Pd), %		64 to 66
Palladium (Pd), %		0

Phosphorus (P), %		0 to 0.0020
Phosphorus (P), %		0 to 0.5

Silicon (Si), %		0
Silicon (Si), %		0 to 1.0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.015

Titanium (Ti), %		0
Titanium (Ti), %		0 to 1.0

Tungsten (W), %		0
Tungsten (W), %		1.0 to 4.0

Zinc (Zn), %		0 to 0.0010
Zinc (Zn), %		0