AWS E16-8-2 vs. Grade CW6M Nickel

AWS E16-8-2 belongs to the iron alloys classification, while grade CW6M nickel belongs to the nickel alloys. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS E16-8-2 and the bottom bar is grade CW6M nickel.

AWS E16-8-2 (W36810) Weld Metal Grade CW6M (J30107) Cast Nickel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		220

Elongation at Break, %		40
Elongation at Break, %		29

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		77
Shear Modulus, GPa		84

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		560

Thermal Properties

Latent Heat of Fusion, J/g		280
Latent Heat of Fusion, J/g		330

Melting Completion (Liquidus), °C		1440
Melting Completion (Liquidus), °C		1530

Melting Onset (Solidus), °C		1400
Melting Onset (Solidus), °C		1470

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		430

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		15
Base Metal Price, % relative		65

Density, g/cm³		7.9
Density, g/cm³		8.8

Embodied Carbon, kg CO₂/kg material		3.2
Embodied Carbon, kg CO₂/kg material		13

Embodied Energy, MJ/kg		45
Embodied Energy, MJ/kg		170

Embodied Water, L/kg		140
Embodied Water, L/kg		300

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		22
Strength to Weight: Axial, points		18

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		17

Thermal Shock Resistance, points		16
Thermal Shock Resistance, points		16

Alloy Composition

Carbon (C), %		0 to 0.1
Carbon (C), %		0 to 0.070

Chromium (Cr), %		14.5 to 16.5
Chromium (Cr), %		17 to 20

Copper (Cu), %		0 to 0.75
Copper (Cu), %		0

Iron (Fe), %		68 to 76.5
Iron (Fe), %		0 to 3.0

Manganese (Mn), %		0.5 to 2.5
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		1.0 to 2.0
Molybdenum (Mo), %		17 to 20

Nickel (Ni), %		7.5 to 9.5
Nickel (Ni), %		54.9 to 66

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 0.6
Silicon (Si), %		0 to 1.0

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030