AWS E209 vs. ASTM A369 Grade FP92
Both AWS E209 and ASTM A369 grade FP92 are iron alloys. They have 69% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is AWS E209 and the bottom bar is ASTM A369 grade FP92.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 17 | |
| 19 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 79 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 260 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1490 |
| Melting Onset (Solidus), °C | 1370 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 21 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 4.4 | |
| 2.8 |
| Embodied Energy, MJ/kg | 63 | |
| 40 |
| Embodied Water, L/kg | 180 | |
| 89 |
Common Calculations
| PREN (Pitting Resistance) | 33 | |
| 14 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 | |
| 25 |
| Strength to Weight: Bending, points | 24 | |
| 22 |
| Thermal Shock Resistance, points | 19 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.020 |
| Boron (B), % | 0 | |
| 0.0010 to 0.0060 |
| Carbon (C), % | 0 to 0.060 | |
| 0.070 to 0.13 |
| Chromium (Cr), % | 20.5 to 24 | |
| 8.5 to 9.5 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 |
| Iron (Fe), % | 51.5 to 64.3 | |
| 85.8 to 89.1 |
| Manganese (Mn), % | 4.0 to 7.0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 1.5 to 3.0 | |
| 0.3 to 0.6 |
| Nickel (Ni), % | 9.5 to 12 | |
| 0 to 0.4 |
| Niobium (Nb), % | 0 | |
| 0.040 to 0.090 |
| Nitrogen (N), % | 0.1 to 0.3 | |
| 0.030 to 0.070 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 1.5 to 2.0 |
| Vanadium (V), % | 0.1 to 0.3 | |
| 0.15 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.010 |