AWS E209 vs. ASTM A387 Grade 11 Steel

Both AWS E209 and ASTM A387 grade 11 steel are iron alloys. They have 61% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E209 and the bottom bar is ASTM A387 grade 11 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
25
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 770
500 to 600

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 14
13

Otherwise Unclassified Properties

Base Metal Price, % relative 21
2.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.4
1.6
Embodied Energy, MJ/kg 63
21
Embodied Water, L/kg 180
53

Common Calculations

PREN (Pitting Resistance) 33
3.1
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
18 to 21
Strength to Weight: Bending, points 24
18 to 20
Thermal Shock Resistance, points 19
15 to 18

Alloy Composition

Carbon (C), % 0 to 0.060
0.050 to 0.17
Chromium (Cr), % 20.5 to 24
1.0 to 1.5
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 51.5 to 64.3
96.2 to 97.6
Manganese (Mn), % 4.0 to 7.0
0.4 to 0.65
Molybdenum (Mo), % 1.5 to 3.0
0.45 to 0.65
Nickel (Ni), % 9.5 to 12
0
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0.5 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0.1 to 0.3
0