AWS E209 vs. AWS E309H

Both AWS E209 and AWS E309H are iron alloys. Both are furnished in the as-welded condition. They have a moderately high 94% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS E209 and the bottom bar is AWS E309H.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
34
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 770
620

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1420
1410
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 14
14

Otherwise Unclassified Properties

Base Metal Price, % relative 21
20
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.4
3.7
Embodied Energy, MJ/kg 63
52
Embodied Water, L/kg 180
180

Common Calculations

PREN (Pitting Resistance) 33
25
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28
22
Strength to Weight: Bending, points 24
21
Thermal Shock Resistance, points 19
16

Alloy Composition

Carbon (C), % 0 to 0.060
0.040 to 0.15
Chromium (Cr), % 20.5 to 24
22 to 25
Copper (Cu), % 0 to 0.75
0 to 0.75
Iron (Fe), % 51.5 to 64.3
55.8 to 65.5
Manganese (Mn), % 4.0 to 7.0
0.5 to 2.5
Molybdenum (Mo), % 1.5 to 3.0
0 to 0.75
Nickel (Ni), % 9.5 to 12
12 to 14
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0.1 to 0.3
0