AWS E209 vs. AWS E316H

Both AWS E209 and AWS E316H are iron alloys. Both are furnished in the as-welded condition. They have a moderately high 92% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS E209 and the bottom bar is AWS E316H.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 770
580

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1370
1390
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 14
14

Otherwise Unclassified Properties

Base Metal Price, % relative 21
20
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.4
4.0
Embodied Energy, MJ/kg 63
55
Embodied Water, L/kg 180
160

Common Calculations

PREN (Pitting Resistance) 33
27
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28
21
Strength to Weight: Bending, points 24
20
Thermal Shock Resistance, points 19
15

Alloy Composition

Carbon (C), % 0 to 0.060
0.040 to 0.080
Chromium (Cr), % 20.5 to 24
17 to 20
Copper (Cu), % 0 to 0.75
0 to 0.75
Iron (Fe), % 51.5 to 64.3
58.6 to 69.5
Manganese (Mn), % 4.0 to 7.0
0.5 to 2.5
Molybdenum (Mo), % 1.5 to 3.0
2.0 to 3.0
Nickel (Ni), % 9.5 to 12
11 to 14
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0.1 to 0.3
0