AWS E209 vs. EN 1.4107 Stainless Steel

Both AWS E209 and EN 1.4107 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E209 and the bottom bar is EN 1.4107 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
18 to 21
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
76
Tensile Strength: Ultimate (UTS), MPa 770
620 to 700

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 14
10

Otherwise Unclassified Properties

Base Metal Price, % relative 21
7.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.4
2.1
Embodied Energy, MJ/kg 63
30
Embodied Water, L/kg 180
100

Common Calculations

PREN (Pitting Resistance) 33
13
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28
22 to 25
Strength to Weight: Bending, points 24
21 to 22
Thermal Shock Resistance, points 19
22 to 25

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.1
Chromium (Cr), % 20.5 to 24
11.5 to 12.5
Copper (Cu), % 0 to 0.75
0 to 0.3
Iron (Fe), % 51.5 to 64.3
83.8 to 87.2
Manganese (Mn), % 4.0 to 7.0
0.5 to 0.8
Molybdenum (Mo), % 1.5 to 3.0
0 to 0.5
Nickel (Ni), % 9.5 to 12
0.8 to 1.5
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0.1 to 0.3
0 to 0.080