AWS E209 vs. EN 1.4874 Stainless Steel

Both AWS E209 and EN 1.4874 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E209 and the bottom bar is EN 1.4874 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 17
6.7
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
80
Tensile Strength: Ultimate (UTS), MPa 770
480

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 480
450
Thermal Expansion, µm/m-K 14
15

Otherwise Unclassified Properties

Base Metal Price, % relative 21
70
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 4.4
7.6
Embodied Energy, MJ/kg 63
110
Embodied Water, L/kg 180
290

Common Calculations

PREN (Pitting Resistance) 33
34
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
16
Strength to Weight: Bending, points 24
16
Thermal Shock Resistance, points 19
11

Alloy Composition

Carbon (C), % 0 to 0.060
0.35 to 0.65
Chromium (Cr), % 20.5 to 24
19 to 22
Cobalt (Co), % 0
18.5 to 22
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 51.5 to 64.3
23 to 38.9
Manganese (Mn), % 4.0 to 7.0
0 to 2.0
Molybdenum (Mo), % 1.5 to 3.0
2.5 to 3.0
Nickel (Ni), % 9.5 to 12
18 to 22
Niobium (Nb), % 0
0.75 to 1.3
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
2.0 to 3.0
Vanadium (V), % 0.1 to 0.3
0