AWS E209 vs. EN 1.5520 Steel

Both AWS E209 and EN 1.5520 steel are iron alloys. They have 59% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS E209 and the bottom bar is EN 1.5520 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
11 to 21
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 770
410 to 1410

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 14
13

Otherwise Unclassified Properties

Base Metal Price, % relative 21
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.4
1.4
Embodied Energy, MJ/kg 63
19
Embodied Water, L/kg 180
48

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
15 to 50
Strength to Weight: Bending, points 24
16 to 36
Thermal Shock Resistance, points 19
12 to 41

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.060
0.15 to 0.2
Chromium (Cr), % 20.5 to 24
0 to 0.3
Copper (Cu), % 0 to 0.75
0 to 0.25
Iron (Fe), % 51.5 to 64.3
97.7 to 98.9
Manganese (Mn), % 4.0 to 7.0
0.9 to 1.2
Molybdenum (Mo), % 1.5 to 3.0
0
Nickel (Ni), % 9.5 to 12
0
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0.1 to 0.3
0