AWS E209 vs. EN 1.8865 Steel

Both AWS E209 and EN 1.8865 steel are iron alloys. They have 61% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS E209 and the bottom bar is EN 1.8865 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
19
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 770
660

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 14
13

Otherwise Unclassified Properties

Base Metal Price, % relative 21
3.2
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.4
1.8
Embodied Energy, MJ/kg 63
24
Embodied Water, L/kg 180
52

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
23
Strength to Weight: Bending, points 24
21
Thermal Shock Resistance, points 19
19

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.060
0 to 0.18
Chromium (Cr), % 20.5 to 24
0 to 1.0
Copper (Cu), % 0 to 0.75
0 to 0.3
Iron (Fe), % 51.5 to 64.3
93.6 to 100
Manganese (Mn), % 4.0 to 7.0
0 to 1.7
Molybdenum (Mo), % 1.5 to 3.0
0 to 0.7
Nickel (Ni), % 9.5 to 12
0 to 1.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0.1 to 0.3
0 to 0.015
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.0050
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0.1 to 0.3
0 to 0.080
Zirconium (Zr), % 0
0 to 0.15