AWS E209 vs. SAE-AISI 1552 Steel

Both AWS E209 and SAE-AISI 1552 steel are iron alloys. They have 59% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS E209 and the bottom bar is SAE-AISI 1552 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
11 to 14
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
72
Tensile Strength: Ultimate (UTS), MPa 770
760 to 840

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 14
11

Otherwise Unclassified Properties

Base Metal Price, % relative 21
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.4
1.4
Embodied Energy, MJ/kg 63
19
Embodied Water, L/kg 180
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
27 to 30
Strength to Weight: Bending, points 24
24 to 25
Thermal Shock Resistance, points 19
26 to 29

Alloy Composition

Carbon (C), % 0 to 0.060
0.47 to 0.55
Chromium (Cr), % 20.5 to 24
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 51.5 to 64.3
97.9 to 98.3
Manganese (Mn), % 4.0 to 7.0
1.2 to 1.5
Molybdenum (Mo), % 1.5 to 3.0
0
Nickel (Ni), % 9.5 to 12
0
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050
Vanadium (V), % 0.1 to 0.3
0