AWS E209 vs. C71640 Copper-nickel
AWS E209 belongs to the iron alloys classification, while C71640 copper-nickel belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS E209 and the bottom bar is C71640 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 140 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 79 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 490 to 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 240 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1180 |
| Melting Onset (Solidus), °C | 1370 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 410 |
| Thermal Expansion, µm/m-K | 14 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 21 | |
| 40 |
| Density, g/cm3 | 7.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 4.4 | |
| 5.0 |
| Embodied Energy, MJ/kg | 63 | |
| 73 |
| Embodied Water, L/kg | 180 | |
| 280 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 8.7 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 28 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 24 | |
| 16 to 18 |
| Thermal Shock Resistance, points | 19 | |
| 16 to 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.060 | |
| 0 |
| Chromium (Cr), % | 20.5 to 24 | |
| 0 |
| Copper (Cu), % | 0 to 0.75 | |
| 61.7 to 67.8 |
| Iron (Fe), % | 51.5 to 64.3 | |
| 1.7 to 2.3 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 4.0 to 7.0 | |
| 1.5 to 2.5 |
| Molybdenum (Mo), % | 1.5 to 3.0 | |
| 0 |
| Nickel (Ni), % | 9.5 to 12 | |
| 29 to 32 |
| Nitrogen (N), % | 0.1 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Vanadium (V), % | 0.1 to 0.3 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |