AWS E209 vs. K93050 Alloy

Both AWS E209 and K93050 alloy are iron alloys. They have 70% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS E209 and the bottom bar is K93050 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 79
72
Tensile Strength: Ultimate (UTS), MPa 770
500 to 680

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1370
1380
Specific Heat Capacity, J/kg-K 480
460
Thermal Expansion, µm/m-K 14
12

Otherwise Unclassified Properties

Base Metal Price, % relative 21
26
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 4.4
4.7
Embodied Energy, MJ/kg 63
65
Embodied Water, L/kg 180
120

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 28
17 to 23
Strength to Weight: Bending, points 24
17 to 21
Thermal Shock Resistance, points 19
16 to 21

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.15
Chromium (Cr), % 20.5 to 24
0 to 0.25
Cobalt (Co), % 0
0 to 0.5
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 51.5 to 64.3
61.4 to 63.9
Manganese (Mn), % 4.0 to 7.0
0 to 1.0
Molybdenum (Mo), % 1.5 to 3.0
0
Nickel (Ni), % 9.5 to 12
36
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Selenium (Se), % 0
0.15 to 0.3
Silicon (Si), % 0 to 1.0
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0.1 to 0.3
0