AWS E209 vs. N08332 Stainless Steel

Both AWS E209 and N08332 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS E209 and the bottom bar is N08332 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
76
Tensile Strength: Ultimate (UTS), MPa 770
520

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Melting Completion (Liquidus), °C 1420
1390
Melting Onset (Solidus), °C 1370
1340
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 14
16

Otherwise Unclassified Properties

Base Metal Price, % relative 21
32
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 4.4
5.4
Embodied Energy, MJ/kg 63
77
Embodied Water, L/kg 180
190

Common Calculations

PREN (Pitting Resistance) 33
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
18
Strength to Weight: Bending, points 24
18
Thermal Shock Resistance, points 19
12

Alloy Composition

Carbon (C), % 0 to 0.060
0.050 to 0.1
Chromium (Cr), % 20.5 to 24
17 to 20
Copper (Cu), % 0 to 0.75
0 to 1.0
Iron (Fe), % 51.5 to 64.3
38.3 to 48.2
Lead (Pb), % 0
0 to 0.0050
Manganese (Mn), % 4.0 to 7.0
0 to 2.0
Molybdenum (Mo), % 1.5 to 3.0
0
Nickel (Ni), % 9.5 to 12
34 to 37
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0.75 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Tin (Sn), % 0
0 to 0.025
Vanadium (V), % 0.1 to 0.3
0