AWS E219 vs. EN 1.4826 Stainless Steel

Both AWS E219 and EN 1.4826 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E219 and the bottom bar is EN 1.4826 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
9.1
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 690
500

Thermal Properties

Latent Heat of Fusion, J/g 290
310
Melting Completion (Liquidus), °C 1400
1400
Melting Onset (Solidus), °C 1360
1360
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 14
14
Thermal Expansion, µm/m-K 15
16

Otherwise Unclassified Properties

Base Metal Price, % relative 15
17
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 3.1
3.3
Embodied Energy, MJ/kg 44
47
Embodied Water, L/kg 160
160

Common Calculations

PREN (Pitting Resistance) 25
23
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 25
18
Strength to Weight: Bending, points 23
18
Thermal Diffusivity, mm2/s 3.8
3.7
Thermal Shock Resistance, points 17
11

Alloy Composition

Carbon (C), % 0 to 0.060
0.3 to 0.5
Chromium (Cr), % 19 to 21.5
21 to 23
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 58.6 to 67.4
60.4 to 68.7
Manganese (Mn), % 8.0 to 10
0 to 2.0
Molybdenum (Mo), % 0 to 0.75
0 to 0.5
Nickel (Ni), % 5.5 to 7.0
9.0 to 11
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
1.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030