AWS E240 vs. AWS E316LMn

Both AWS E240 and AWS E316LMn are iron alloys. Both are furnished in the as-welded condition. They have 84% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS E240 and the bottom bar is AWS E316LMn.

AWS E240 (W32410) Weld Metal AWS E316LMn (W31622) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		17
Elongation at Break, %		23

Poisson's Ratio		0.28
Poisson's Ratio		0.28

Shear Modulus, GPa		77
Shear Modulus, GPa		79

Tensile Strength: Ultimate (UTS), MPa		770
Tensile Strength: Ultimate (UTS), MPa		620

Thermal Properties

Latent Heat of Fusion, J/g		290
Latent Heat of Fusion, J/g		300

Melting Completion (Liquidus), °C		1390
Melting Completion (Liquidus), °C		1420

Melting Onset (Solidus), °C		1350
Melting Onset (Solidus), °C		1370

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		15
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		14
Base Metal Price, % relative		24

Density, g/cm³		7.7
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		3.0
Embodied Carbon, kg CO₂/kg material		4.6

Embodied Energy, MJ/kg		42
Embodied Energy, MJ/kg		64

Embodied Water, L/kg		160
Embodied Water, L/kg		180

Common Calculations

PREN (Pitting Resistance)		22
PREN (Pitting Resistance)		32

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		28
Strength to Weight: Axial, points		22

Strength to Weight: Bending, points		24
Strength to Weight: Bending, points		20

Thermal Shock Resistance, points		19
Thermal Shock Resistance, points		15

Alloy Composition

Carbon (C), %		0 to 0.060
Carbon (C), %		0 to 0.040

Chromium (Cr), %		17 to 19
Chromium (Cr), %		18 to 21

Copper (Cu), %		0 to 0.75
Copper (Cu), %		0 to 0.75

Iron (Fe), %		58.6 to 68.4
Iron (Fe), %		47.5 to 59.4

Manganese (Mn), %		10.5 to 13.5
Manganese (Mn), %		5.0 to 8.0

Molybdenum (Mo), %		0 to 0.75
Molybdenum (Mo), %		2.5 to 3.5

Nickel (Ni), %		4.0 to 6.0
Nickel (Ni), %		15 to 18

Nitrogen (N), %		0.1 to 0.3
Nitrogen (N), %		0.1 to 0.25

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0 to 0.9

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030