AWS E2593 vs. ASTM A182 Grade F10

Both AWS E2593 and ASTM A182 grade F10 are iron alloys. They have 76% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS E2593 and the bottom bar is ASTM A182 grade F10.

AWS E2593 (W39593) Weld Metal ASTM A182 Grade F10 (S33100) Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		190

Elongation at Break, %		17
Elongation at Break, %		34

Poisson's Ratio		0.27
Poisson's Ratio		0.29

Shear Modulus, GPa		80
Shear Modulus, GPa		74

Tensile Strength: Ultimate (UTS), MPa		850
Tensile Strength: Ultimate (UTS), MPa		630

Thermal Properties

Latent Heat of Fusion, J/g		300
Latent Heat of Fusion, J/g		290

Melting Completion (Liquidus), °C		1430
Melting Completion (Liquidus), °C		1420

Melting Onset (Solidus), °C		1390
Melting Onset (Solidus), °C		1370

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		22
Base Metal Price, % relative		18

Density, g/cm³		7.8
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		4.2
Embodied Carbon, kg CO₂/kg material		3.6

Embodied Energy, MJ/kg		59
Embodied Energy, MJ/kg		51

Embodied Water, L/kg		190
Embodied Water, L/kg		120

Common Calculations

PREN (Pitting Resistance)		39
PREN (Pitting Resistance)		8.0

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		30
Strength to Weight: Axial, points		22

Strength to Weight: Bending, points		25
Strength to Weight: Bending, points		21

Thermal Shock Resistance, points		21
Thermal Shock Resistance, points		18

Alloy Composition

Carbon (C), %		0 to 0.040
Carbon (C), %		0.1 to 0.2

Chromium (Cr), %		24 to 27
Chromium (Cr), %		7.0 to 9.0

Copper (Cu), %		1.5 to 3.0
Copper (Cu), %		0

Iron (Fe), %		52.7 to 62.5
Iron (Fe), %		66.5 to 72.4

Manganese (Mn), %		0.5 to 1.5
Manganese (Mn), %		0.5 to 0.8

Molybdenum (Mo), %		2.9 to 3.9
Molybdenum (Mo), %		0

Nickel (Ni), %		8.5 to 10.5
Nickel (Ni), %		19 to 22

Nitrogen (N), %		0.080 to 0.25
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 1.0
Silicon (Si), %		1.0 to 1.4

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030