AWS E2593 vs. AWS E310

Both AWS E2593 and AWS E310 are iron alloys. Both are furnished in the as-welded condition. They have 86% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS E2593 and the bottom bar is AWS E310.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
34
Poisson's Ratio 0.27
0.27
Shear Modulus, GPa 80
79
Tensile Strength: Ultimate (UTS), MPa 850
620

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1430
1400
Melting Onset (Solidus), °C 1390
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 16
14
Thermal Expansion, µm/m-K 14
14

Otherwise Unclassified Properties

Base Metal Price, % relative 22
26
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.2
4.6
Embodied Energy, MJ/kg 59
65
Embodied Water, L/kg 190
200

Common Calculations

PREN (Pitting Resistance) 39
28
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
22
Strength to Weight: Bending, points 25
20
Thermal Diffusivity, mm2/s 4.3
3.7
Thermal Shock Resistance, points 21
15

Alloy Composition

Carbon (C), % 0 to 0.040
0.080 to 0.2
Chromium (Cr), % 24 to 27
25 to 28
Copper (Cu), % 1.5 to 3.0
0 to 0.75
Iron (Fe), % 52.7 to 62.5
44.5 to 53.9
Manganese (Mn), % 0.5 to 1.5
1.0 to 2.5
Molybdenum (Mo), % 2.9 to 3.9
0 to 0.75
Nickel (Ni), % 8.5 to 10.5
20 to 22.5
Nitrogen (N), % 0.080 to 0.25
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030