AWS E2593 vs. Grade 3 Babbitt Metal

AWS E2593 belongs to the iron alloys classification, while grade 3 Babbitt Metal belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS E2593 and the bottom bar is grade 3 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
56
Poisson's Ratio 0.27
0.35
Shear Modulus, GPa 80
21

Thermal Properties

Latent Heat of Fusion, J/g 300
79
Melting Completion (Liquidus), °C 1430
420
Melting Onset (Solidus), °C 1390
240
Specific Heat Capacity, J/kg-K 470
230
Thermal Expansion, µm/m-K 14
21

Otherwise Unclassified Properties

Base Metal Price, % relative 22
70
Density, g/cm3 7.8
7.4
Embodied Carbon, kg CO2/kg material 4.2
12
Embodied Energy, MJ/kg 59
200
Embodied Water, L/kg 190
1210

Common Calculations

Stiffness to Weight: Axial, points 14
4.2
Stiffness to Weight: Bending, points 25
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
7.5 to 8.5
Arsenic (As), % 0
0 to 0.1
Bismuth (Bi), % 0
0 to 0.080
Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0 to 0.040
0
Chromium (Cr), % 24 to 27
0
Copper (Cu), % 1.5 to 3.0
7.5 to 8.5
Iron (Fe), % 52.7 to 62.5
0 to 0.080
Lead (Pb), % 0
0 to 0.35
Manganese (Mn), % 0.5 to 1.5
0
Molybdenum (Mo), % 2.9 to 3.9
0
Nickel (Ni), % 8.5 to 10.5
0
Nitrogen (N), % 0.080 to 0.25
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
82.3 to 85
Zinc (Zn), % 0
0 to 0.0050