AWS E307 vs. C77000 Nickel Silver
AWS E307 belongs to the iron alloys classification, while C77000 nickel silver belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AWS E307 and the bottom bar is C77000 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 78 | |
| 46 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 420 to 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 200 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1050 |
| Melting Onset (Solidus), °C | 1370 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 400 |
| Thermal Conductivity, W/m-K | 15 | |
| 29 |
| Thermal Expansion, µm/m-K | 14 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.1 | |
| 5.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 6.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 17 | |
| 31 |
| Density, g/cm3 | 7.8 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 3.5 | |
| 4.1 |
| Embodied Energy, MJ/kg | 49 | |
| 63 |
| Embodied Water, L/kg | 160 | |
| 300 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 24 | |
| 14 to 27 |
| Strength to Weight: Bending, points | 22 | |
| 15 to 23 |
| Thermal Diffusivity, mm2/s | 4.1 | |
| 8.8 |
| Thermal Shock Resistance, points | 17 | |
| 15 to 28 |
Alloy Composition
| Carbon (C), % | 0.040 to 0.14 | |
| 0 |
| Chromium (Cr), % | 18 to 21.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.75 | |
| 53.5 to 56.5 |
| Iron (Fe), % | 59.6 to 69.2 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 3.3 to 4.8 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0.5 to 1.5 | |
| 0 |
| Nickel (Ni), % | 9.0 to 10.7 | |
| 16.5 to 19.5 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 22.7 to 30 |
| Residuals, % | 0 | |
| 0 to 0.5 |