AWS E307 vs. S21460 Stainless Steel

Both AWS E307 and S21460 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS E307 and the bottom bar is S21460 stainless steel.

AWS E307 (W30710) Weld Metal UNS S21460 (XM-14) Stainless Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		34
Elongation at Break, %		46

Poisson's Ratio		0.28
Poisson's Ratio		0.28

Shear Modulus, GPa		78
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		660
Tensile Strength: Ultimate (UTS), MPa		830

Thermal Properties

Latent Heat of Fusion, J/g		290
Latent Heat of Fusion, J/g		290

Melting Completion (Liquidus), °C		1420
Melting Completion (Liquidus), °C		1380

Melting Onset (Solidus), °C		1370
Melting Onset (Solidus), °C		1330

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		18

Otherwise Unclassified Properties

Base Metal Price, % relative		17
Base Metal Price, % relative		14

Density, g/cm³		7.8
Density, g/cm³		7.6

Embodied Carbon, kg CO₂/kg material		3.5
Embodied Carbon, kg CO₂/kg material		3.0

Embodied Energy, MJ/kg		49
Embodied Energy, MJ/kg		43

Embodied Water, L/kg		160
Embodied Water, L/kg		160

Common Calculations

PREN (Pitting Resistance)		23
PREN (Pitting Resistance)		25

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		24
Strength to Weight: Axial, points		30

Strength to Weight: Bending, points		22
Strength to Weight: Bending, points		26

Thermal Shock Resistance, points		17
Thermal Shock Resistance, points		17

Alloy Composition

Carbon (C), %		0.040 to 0.14
Carbon (C), %		0 to 0.12

Chromium (Cr), %		18 to 21.5
Chromium (Cr), %		17 to 19

Copper (Cu), %		0 to 0.75
Copper (Cu), %		0

Iron (Fe), %		59.6 to 69.2
Iron (Fe), %		57.3 to 63.7

Manganese (Mn), %		3.3 to 4.8
Manganese (Mn), %		14 to 16

Molybdenum (Mo), %		0.5 to 1.5
Molybdenum (Mo), %		0

Nickel (Ni), %		9.0 to 10.7
Nickel (Ni), %		5.0 to 6.0

Nitrogen (N), %		0
Nitrogen (N), %		0.35 to 0.5

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.060

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0 to 1.0

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030