AWS E310Mo vs. EN 1.4841 Stainless Steel

Both AWS E310Mo and EN 1.4841 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E310Mo and the bottom bar is EN 1.4841 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
32
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 620
650

Thermal Properties

Latent Heat of Fusion, J/g 310
330
Melting Completion (Liquidus), °C 1420
1380
Melting Onset (Solidus), °C 1370
1340
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 14
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 28
25
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.1
4.3
Embodied Energy, MJ/kg 71
62
Embodied Water, L/kg 210
190

Common Calculations

PREN (Pitting Resistance) 35
26
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
23
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 3.7
4.0
Thermal Shock Resistance, points 15
15

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.2
Chromium (Cr), % 25 to 28
24 to 26
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 42.8 to 52
47.1 to 55.5
Manganese (Mn), % 1.0 to 2.5
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 20 to 22
19 to 22
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.75
1.5 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.015