AWS E310Nb vs. Type 2 Magnetic Alloy

Both AWS E310Nb and Type 2 magnetic alloy are iron alloys. They have 71% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E310Nb and the bottom bar is Type 2 magnetic alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 29
2.0 to 38
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 79
72
Tensile Strength: Ultimate (UTS), MPa 620
510 to 910

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Melting Completion (Liquidus), °C 1410
1420
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 480
460
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
3.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
4.2

Otherwise Unclassified Properties

Base Metal Price, % relative 31
33
Density, g/cm3 7.9
8.4
Embodied Carbon, kg CO2/kg material 5.3
5.9
Embodied Energy, MJ/kg 76
81
Embodied Water, L/kg 200
140

Common Calculations

Stiffness to Weight: Axial, points 14
12
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 22
17 to 30
Strength to Weight: Bending, points 20
17 to 25
Thermal Shock Resistance, points 15
16 to 29

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.050
Chromium (Cr), % 25 to 28
0 to 0.3
Cobalt (Co), % 0
0 to 0.5
Copper (Cu), % 0 to 0.75
0 to 0.3
Iron (Fe), % 44.1 to 53.3
48.2 to 53
Manganese (Mn), % 1.0 to 2.5
0 to 0.8
Molybdenum (Mo), % 0 to 0.75
0 to 0.3
Nickel (Ni), % 20 to 22
47 to 49
Niobium (Nb), % 0.7 to 1.0
0
Phosphorus (P), % 0 to 0.030
0 to 0.010
Silicon (Si), % 0 to 0.75
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030