AWS E3155 vs. AISI 405 Stainless Steel

Both AWS E3155 and AISI 405 stainless steel are iron alloys. They have 44% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS E3155 and the bottom bar is AISI 405 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 23
22
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 81
76
Tensile Strength: Ultimate (UTS), MPa 770
470

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Melting Completion (Liquidus), °C 1460
1530
Melting Onset (Solidus), °C 1410
1480
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 13
30
Thermal Expansion, µm/m-K 13
11

Otherwise Unclassified Properties

Base Metal Price, % relative 70
7.0
Density, g/cm3 8.4
7.7
Embodied Carbon, kg CO2/kg material 7.7
2.0
Embodied Energy, MJ/kg 110
28
Embodied Water, L/kg 300
100

Common Calculations

PREN (Pitting Resistance) 35
13
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 26
17
Strength to Weight: Bending, points 22
17
Thermal Diffusivity, mm2/s 3.3
8.1
Thermal Shock Resistance, points 20
16

Alloy Composition

Aluminum (Al), % 0
0.1 to 0.3
Carbon (C), % 0 to 0.1
0 to 0.080
Chromium (Cr), % 20 to 22.5
11.5 to 14.5
Cobalt (Co), % 18.5 to 21
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 23.3 to 36.3
82.5 to 88.4
Manganese (Mn), % 1.0 to 2.5
0 to 1.0
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 19 to 21
0 to 0.6
Niobium (Nb), % 0.75 to 1.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 2.0 to 3.0
0