AWS E3155 vs. EN 1.4105 Stainless Steel

Both AWS E3155 and EN 1.4105 stainless steel are iron alloys. They have 49% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS E3155 and the bottom bar is EN 1.4105 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 23
23
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 81
77
Tensile Strength: Ultimate (UTS), MPa 770
530

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1410
1390
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 13
25
Thermal Expansion, µm/m-K 13
10

Otherwise Unclassified Properties

Base Metal Price, % relative 70
9.0
Density, g/cm3 8.4
7.7
Embodied Carbon, kg CO2/kg material 7.7
2.2
Embodied Energy, MJ/kg 110
31
Embodied Water, L/kg 300
120

Common Calculations

PREN (Pitting Resistance) 35
18
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 26
19
Strength to Weight: Bending, points 22
19
Thermal Diffusivity, mm2/s 3.3
6.7
Thermal Shock Resistance, points 20
19

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.080
Chromium (Cr), % 20 to 22.5
16 to 18
Cobalt (Co), % 18.5 to 21
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 23.3 to 36.3
77.9 to 83.7
Manganese (Mn), % 1.0 to 2.5
0 to 1.5
Molybdenum (Mo), % 2.5 to 3.5
0.2 to 0.6
Nickel (Ni), % 19 to 21
0
Niobium (Nb), % 0.75 to 1.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.030
0.15 to 0.35
Tungsten (W), % 2.0 to 3.0
0