AWS E3155 vs. EN 1.4469 Stainless Steel

Both AWS E3155 and EN 1.4469 stainless steel are iron alloys. They have 62% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E3155 and the bottom bar is EN 1.4469 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
210
Elongation at Break, % 23
25
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 81
81
Tensile Strength: Ultimate (UTS), MPa 770
740

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 13
17
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Base Metal Price, % relative 70
21
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 7.7
4.1
Embodied Energy, MJ/kg 110
57
Embodied Water, L/kg 300
180

Common Calculations

PREN (Pitting Resistance) 35
42
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 26
26
Strength to Weight: Bending, points 22
23
Thermal Diffusivity, mm2/s 3.3
4.6
Thermal Shock Resistance, points 20
20

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.030
Chromium (Cr), % 20 to 22.5
25 to 27
Cobalt (Co), % 18.5 to 21
0
Copper (Cu), % 0 to 0.75
0 to 1.3
Iron (Fe), % 23.3 to 36.3
56.4 to 65.9
Manganese (Mn), % 1.0 to 2.5
0 to 1.0
Molybdenum (Mo), % 2.5 to 3.5
3.0 to 5.0
Nickel (Ni), % 19 to 21
6.0 to 8.0
Niobium (Nb), % 0.75 to 1.3
0
Nitrogen (N), % 0
0.12 to 0.22
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.025
Tungsten (W), % 2.0 to 3.0
0