AWS E3155 vs. EN 1.4508 Stainless Steel

Both AWS E3155 and EN 1.4508 stainless steel are iron alloys. They have 64% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E3155 and the bottom bar is EN 1.4508 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 23
34
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 81
79
Tensile Strength: Ultimate (UTS), MPa 770
570

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
15
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 70
20
Density, g/cm3 8.4
7.9
Embodied Carbon, kg CO2/kg material 7.7
4.0
Embodied Energy, MJ/kg 110
55
Embodied Water, L/kg 300
160

Common Calculations

PREN (Pitting Resistance) 35
32
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 26
20
Strength to Weight: Bending, points 22
19
Thermal Diffusivity, mm2/s 3.3
4.1
Thermal Shock Resistance, points 20
17

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.030
Chromium (Cr), % 20 to 22.5
18 to 20
Cobalt (Co), % 18.5 to 21
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 23.3 to 36.3
61.2 to 69.9
Manganese (Mn), % 1.0 to 2.5
0 to 1.5
Molybdenum (Mo), % 2.5 to 3.5
3.0 to 3.5
Nickel (Ni), % 19 to 21
9.0 to 12
Niobium (Nb), % 0.75 to 1.3
0
Nitrogen (N), % 0
0.1 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 2.0 to 3.0
0