AWS E316LMn vs. Grade M30C Nickel

AWS E316LMn belongs to the iron alloys classification, while grade M30C nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS E316LMn and the bottom bar is grade M30C nickel.

AWS E316LMn (W31622) Weld Metal Grade M30C (J24130) Cast Nickel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		160

Elongation at Break, %		23
Elongation at Break, %		29

Poisson's Ratio		0.28
Poisson's Ratio		0.32

Shear Modulus, GPa		79
Shear Modulus, GPa		61

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		510

Thermal Properties

Latent Heat of Fusion, J/g		300
Latent Heat of Fusion, J/g		290

Melting Completion (Liquidus), °C		1420
Melting Completion (Liquidus), °C		1290

Melting Onset (Solidus), °C		1370
Melting Onset (Solidus), °C		1240

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		430

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		24
Base Metal Price, % relative		60

Density, g/cm³		7.9
Density, g/cm³		8.8

Embodied Carbon, kg CO₂/kg material		4.6
Embodied Carbon, kg CO₂/kg material		9.5

Embodied Energy, MJ/kg		64
Embodied Energy, MJ/kg		140

Embodied Water, L/kg		180
Embodied Water, L/kg		250

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		10

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		21

Strength to Weight: Axial, points		22
Strength to Weight: Axial, points		16

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		16

Thermal Shock Resistance, points		15
Thermal Shock Resistance, points		18

Alloy Composition

Carbon (C), %		0 to 0.040
Carbon (C), %		0 to 0.3

Chromium (Cr), %		18 to 21
Chromium (Cr), %		0

Copper (Cu), %		0 to 0.75
Copper (Cu), %		26 to 33

Iron (Fe), %		47.5 to 59.4
Iron (Fe), %		0 to 3.5

Manganese (Mn), %		5.0 to 8.0
Manganese (Mn), %		0 to 1.5

Molybdenum (Mo), %		2.5 to 3.5
Molybdenum (Mo), %		0

Nickel (Ni), %		15 to 18
Nickel (Ni), %		56.6 to 72

Niobium (Nb), %		0
Niobium (Nb), %		1.0 to 3.0

Nitrogen (N), %		0.1 to 0.25
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 0.9
Silicon (Si), %		1.0 to 2.0

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030