AWS E316LMn vs. S82441 Stainless Steel

Both AWS E316LMn and S82441 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS E316LMn and the bottom bar is S82441 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 23
28
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 79
79
Tensile Strength: Ultimate (UTS), MPa 620
760

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1370
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 14
13

Otherwise Unclassified Properties

Base Metal Price, % relative 24
16
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.6
3.2
Embodied Energy, MJ/kg 64
45
Embodied Water, L/kg 180
170

Common Calculations

PREN (Pitting Resistance) 32
33
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
27
Strength to Weight: Bending, points 20
24
Thermal Shock Resistance, points 15
21

Alloy Composition

Carbon (C), % 0 to 0.040
0 to 0.030
Chromium (Cr), % 18 to 21
23 to 25
Copper (Cu), % 0 to 0.75
0.1 to 0.8
Iron (Fe), % 47.5 to 59.4
62.6 to 70.2
Manganese (Mn), % 5.0 to 8.0
2.5 to 4.0
Molybdenum (Mo), % 2.5 to 3.5
1.0 to 2.0
Nickel (Ni), % 15 to 18
3.0 to 4.5
Nitrogen (N), % 0.1 to 0.25
0.2 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 0.9
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.0050