AWS E330H vs. N06060 Nickel

AWS E330H belongs to the iron alloys classification, while N06060 nickel belongs to the nickel alloys. They have 59% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E330H and the bottom bar is N06060 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 11
45
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 76
82
Tensile Strength: Ultimate (UTS), MPa 690
700

Thermal Properties

Latent Heat of Fusion, J/g 290
320
Melting Completion (Liquidus), °C 1400
1510
Melting Onset (Solidus), °C 1350
1450
Specific Heat Capacity, J/kg-K 470
430
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 30
65
Density, g/cm3 8.1
8.7
Embodied Carbon, kg CO2/kg material 5.4
12
Embodied Energy, MJ/kg 76
160
Embodied Water, L/kg 180
280

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 24
22
Strength to Weight: Bending, points 22
20
Thermal Shock Resistance, points 19
19

Alloy Composition

Carbon (C), % 0.35 to 0.45
0 to 0.030
Chromium (Cr), % 14 to 17
19 to 22
Copper (Cu), % 0 to 0.75
0.25 to 1.3
Iron (Fe), % 40.5 to 51.7
0 to 14
Manganese (Mn), % 1.0 to 2.5
0 to 1.5
Molybdenum (Mo), % 0 to 0.75
12 to 14
Nickel (Ni), % 33 to 37
54 to 60
Niobium (Nb), % 0
0.5 to 1.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.0050
Tungsten (W), % 0
0.25 to 1.3