AWS E347 vs. ACI-ASTM CF16F Steel

Both AWS E347 and ACI-ASTM CF16F steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E347 and the bottom bar is ACI-ASTM CF16F steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
50
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 580
530

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
16
Thermal Expansion, µm/m-K 14
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 19
18
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.7
3.4
Embodied Energy, MJ/kg 53
47
Embodied Water, L/kg 150
150

Common Calculations

PREN (Pitting Resistance) 21
22
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 4.2
4.3
Thermal Shock Resistance, points 15
12

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.16
Chromium (Cr), % 18 to 21
18 to 21
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 61.9 to 72.5
61.3 to 72.8
Manganese (Mn), % 0.5 to 2.5
0 to 1.5
Molybdenum (Mo), % 0 to 0.75
0 to 1.5
Nickel (Ni), % 9.0 to 11
9.0 to 12
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.17
Selenium (Se), % 0
0.2 to 0.35
Silicon (Si), % 0 to 1.0
0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.040