AWS E347 vs. N08926 Stainless Steel

Both AWS E347 and N08926 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E347 and the bottom bar is N08926 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
40
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
80
Tensile Strength: Ultimate (UTS), MPa 580
740

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 16
12
Thermal Expansion, µm/m-K 14
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 19
33
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.7
6.2
Embodied Energy, MJ/kg 53
84
Embodied Water, L/kg 150
200

Common Calculations

PREN (Pitting Resistance) 21
45
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
25
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 4.2
3.2
Thermal Shock Resistance, points 15
16

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.020
Chromium (Cr), % 18 to 21
19 to 21
Copper (Cu), % 0 to 0.75
0.5 to 1.5
Iron (Fe), % 61.9 to 72.5
41.7 to 50.4
Manganese (Mn), % 0.5 to 2.5
0 to 2.0
Molybdenum (Mo), % 0 to 0.75
6.0 to 7.0
Nickel (Ni), % 9.0 to 11
24 to 26
Niobium (Nb), % 0 to 1.0
0
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010