AWS E347 vs. N10001 Nickel

AWS E347 belongs to the iron alloys classification, while N10001 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS E347 and the bottom bar is N10001 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
220
Elongation at Break, % 34
45
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 77
84
Tensile Strength: Ultimate (UTS), MPa 580
780

Thermal Properties

Latent Heat of Fusion, J/g 290
320
Melting Completion (Liquidus), °C 1430
1620
Melting Onset (Solidus), °C 1380
1570
Specific Heat Capacity, J/kg-K 480
390
Thermal Expansion, µm/m-K 14
10

Otherwise Unclassified Properties

Base Metal Price, % relative 19
75
Density, g/cm3 7.8
9.2
Embodied Carbon, kg CO2/kg material 3.7
15
Embodied Energy, MJ/kg 53
200
Embodied Water, L/kg 150
260

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 21
24
Strength to Weight: Bending, points 20
21
Thermal Shock Resistance, points 15
25

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.050
Chromium (Cr), % 18 to 21
0 to 1.0
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 61.9 to 72.5
4.0 to 6.0
Manganese (Mn), % 0.5 to 2.5
0 to 1.0
Molybdenum (Mo), % 0 to 0.75
26 to 30
Nickel (Ni), % 9.0 to 11
58 to 69.8
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0
0.2 to 0.4