AWS E383 vs. AISI 301 Stainless Steel

Both AWS E383 and AISI 301 stainless steel are iron alloys. They have 59% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E383 and the bottom bar is AISI 301 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 34
7.4 to 46
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Tensile Strength: Ultimate (UTS), MPa 580
590 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 320
280
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 14
17

Otherwise Unclassified Properties

Base Metal Price, % relative 37
13
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.4
2.7
Embodied Energy, MJ/kg 89
39
Embodied Water, L/kg 240
130

Common Calculations

PREN (Pitting Resistance) 40
18
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
21 to 52
Strength to Weight: Bending, points 19
20 to 37
Thermal Diffusivity, mm2/s 3.1
4.2
Thermal Shock Resistance, points 15
12 to 31

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 26.5 to 29
16 to 18
Copper (Cu), % 0.6 to 1.5
0
Iron (Fe), % 28.8 to 39.2
70.7 to 78
Manganese (Mn), % 0.5 to 2.5
0 to 2.0
Molybdenum (Mo), % 3.2 to 4.2
0
Nickel (Ni), % 30 to 33
6.0 to 8.0
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.030