AWS E383 vs. AISI 334 Stainless Steel

Both AWS E383 and AISI 334 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E383 and the bottom bar is AISI 334 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 34
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Tensile Strength: Ultimate (UTS), MPa 580
540

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Melting Completion (Liquidus), °C 1420
1410
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 14
16

Otherwise Unclassified Properties

Base Metal Price, % relative 37
22
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.4
4.1
Embodied Energy, MJ/kg 89
59
Embodied Water, L/kg 240
170

Common Calculations

PREN (Pitting Resistance) 40
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
19
Strength to Weight: Bending, points 19
19
Thermal Shock Resistance, points 15
12

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 26.5 to 29
18 to 20
Copper (Cu), % 0.6 to 1.5
0
Iron (Fe), % 28.8 to 39.2
55.7 to 62.7
Manganese (Mn), % 0.5 to 2.5
0 to 1.0
Molybdenum (Mo), % 3.2 to 4.2
0
Nickel (Ni), % 30 to 33
19 to 21
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6