AWS E383 vs. EN 1.3555 Steel

Both AWS E383 and EN 1.3555 steel are iron alloys. They have 46% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E383 and the bottom bar is EN 1.3555 steel.

AWS E383 (W88028) Weld Metal EN 1.3555 (13MoCrNi42-16-14) High-Temperature Bearing Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		210
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		80
Shear Modulus, GPa		75

Tensile Strength: Ultimate (UTS), MPa		580
Tensile Strength: Ultimate (UTS), MPa		770

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		1420
Melting Completion (Liquidus), °C		1500

Melting Onset (Solidus), °C		1370
Melting Onset (Solidus), °C		1450

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		460

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		37
Base Metal Price, % relative		11

Density, g/cm³		8.1
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		6.4
Embodied Carbon, kg CO₂/kg material		5.6

Embodied Energy, MJ/kg		89
Embodied Energy, MJ/kg		81

Embodied Water, L/kg		240
Embodied Water, L/kg		90

Common Calculations

PREN (Pitting Resistance)		40
PREN (Pitting Resistance)		18

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		20
Strength to Weight: Axial, points		27

Strength to Weight: Bending, points		19
Strength to Weight: Bending, points		23

Thermal Shock Resistance, points		15
Thermal Shock Resistance, points		22

Alloy Composition

Carbon (C), %		0 to 0.030
Carbon (C), %		0.1 to 0.15

Chromium (Cr), %		26.5 to 29
Chromium (Cr), %		3.9 to 4.3

Copper (Cu), %		0.6 to 1.5
Copper (Cu), %		0 to 0.1

Iron (Fe), %		28.8 to 39.2
Iron (Fe), %		85.4 to 87.7

Manganese (Mn), %		0.5 to 2.5
Manganese (Mn), %		0.15 to 0.35

Molybdenum (Mo), %		3.2 to 4.2
Molybdenum (Mo), %		4.0 to 4.5

Nickel (Ni), %		30 to 33
Nickel (Ni), %		3.2 to 3.6

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0 to 0.015

Silicon (Si), %		0 to 0.9
Silicon (Si), %		0.1 to 0.25

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0 to 0.010

Tungsten (W), %		0
Tungsten (W), %		0 to 0.15

Vanadium (V), %		0
Vanadium (V), %		1.0 to 1.3