AWS E383 vs. EN 1.4982 Stainless Steel

Both AWS E383 and EN 1.4982 stainless steel are iron alloys. They have 62% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E383 and the bottom bar is EN 1.4982 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 34
28
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 580
750

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1370
1390
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
13
Thermal Expansion, µm/m-K 14
16

Otherwise Unclassified Properties

Base Metal Price, % relative 37
22
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.4
4.9
Embodied Energy, MJ/kg 89
71
Embodied Water, L/kg 240
150

Common Calculations

PREN (Pitting Resistance) 40
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
27
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 3.1
3.4
Thermal Shock Resistance, points 15
17

Alloy Composition

Boron (B), % 0
0.0030 to 0.0090
Carbon (C), % 0 to 0.030
0.070 to 0.13
Chromium (Cr), % 26.5 to 29
14 to 16
Copper (Cu), % 0.6 to 1.5
0
Iron (Fe), % 28.8 to 39.2
61.8 to 69.7
Manganese (Mn), % 0.5 to 2.5
5.5 to 7.0
Molybdenum (Mo), % 3.2 to 4.2
0.8 to 1.2
Nickel (Ni), % 30 to 33
9.0 to 11
Niobium (Nb), % 0
0.75 to 1.3
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.030
Vanadium (V), % 0
0.15 to 0.4