AWS E383 vs. Grey Cast Iron
Both AWS E383 and grey cast iron are iron alloys. They have a modest 35% of their average alloy composition in common, which, by itself, doesn't mean much. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS E383 and the bottom bar is grey cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 180 |
| Elongation at Break, % | 34 | |
| 9.6 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 69 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 160 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 280 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1380 |
| Melting Onset (Solidus), °C | 1370 | |
| 1180 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 490 |
| Thermal Conductivity, W/m-K | 12 | |
| 46 |
| Thermal Expansion, µm/m-K | 14 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 1.9 |
| Density, g/cm3 | 8.1 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 6.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 89 | |
| 21 |
| Embodied Water, L/kg | 240 | |
| 44 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 5.8 to 17 |
| Strength to Weight: Bending, points | 19 | |
| 8.7 to 17 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 13 |
| Thermal Shock Resistance, points | 15 | |
| 6.0 to 17 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 3.1 to 3.4 |
| Chromium (Cr), % | 26.5 to 29 | |
| 0 |
| Copper (Cu), % | 0.6 to 1.5 | |
| 0 |
| Iron (Fe), % | 28.8 to 39.2 | |
| 92.1 to 93.9 |
| Manganese (Mn), % | 0.5 to 2.5 | |
| 0.5 to 0.7 |
| Molybdenum (Mo), % | 3.2 to 4.2 | |
| 0 |
| Nickel (Ni), % | 30 to 33 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.9 |
| Silicon (Si), % | 0 to 0.9 | |
| 2.5 to 2.8 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.15 |